| Property |
HF |
HFA |
| API Gravity, °API, ASTM D287 |
29 |
30 |
| Acid Number, mgKOH/g, ASTM D664 |
|
0.03 (0.2 max) |
| Barium, mg/kg, ASTM D5185 |
<1 (10 max) |
|
| Base Oil Specific Gravity 15.6 C/15.6 C, ASTM D287 |
0.872 |
|
| Bulk Modulus, Isothermal secant at 40 C/4000 psi, psi, ASTM D6793 |
200,000 min |
200,000 min |
| Color, Visual |
Red |
Red |
| Copper Strip Corrosion, 72 hrs at 135 C, ASTM D130 |
1B (2E max) |
1B (2E max) |
| Corrosion and Oxidation Stability, 168 hours at 135 C, Rating, ASTM D4636 |
PASS |
PASS |
| Density @ 60 F, lb/gal, CALCULATED |
7.26 |
7.26 |
| Evapor. Loss, 6H at 71C, mass %, ASTM D972 |
12 (20 max) |
|
| Flash Point, Cleveland Open Cup, °C, ASTM D92 |
107 |
107 (93 min) |
| Flash Point, Pensky-Martens Closed Cup, °C, ASTM D93 |
96 (82 min) |
92 |
| Foam, Sequence I, Stability, ml, ASTM D892 |
|
0 |
| Foam, Sequence I, Tendency, ml, ASTM D892 |
|
36 (65 max) |
| Four-Ball Wear Test, Scar Diameter, mm, ASTM D4172 |
0.6 (1.0 max) |
|
| Four-Ball Wear Test, Scar Diameter, 40 kg, 1200 rpm, 1 h, 75 C, mm, ASTM D4172 |
|
0.6 (1.0 max) |
| Kinematic Viscosity -40 F, cSt, ASTM D445 |
|
450 (500 max) |
| Kinematic Viscosity 130 F, cSt, ASTM D445 |
|
10.4 (10.0 min) |
| Kinematic Viscosity @ -40 C, mm2/s, ASTM D445 |
450 (600 max) |
|
| Kinematic Viscosity @ -54 C, mm2/s, ASTM D445 |
2000 (2500 max) |
1900 |
| Kinematic Viscosity @ 100 C, mm2/s, ASTM D445 |
5.2 (4.9 min) |
5.2 |
| Kinematic Viscosity @ 40 C, mm2/s, ASTM D445 |
14.0 (13.2 min) |
14.0 |
| Low Temperature Stability, 72 hrs @ – 54 C, FTM 3459 |
|
PASS |
| Low Temperature Stability, 72 hrs @ – 54 C, FTM 791.3458 |
PASS |
|
| Particulate Contamination, mg/100ml, ASTM D4898 |
0.2 (0.3 max) |
|
| Pour Point, °C, ASTM D97 |
-62 (-60 max) |
-64 (-60 max) |
| Shear Stability, %KV loss, ASTM D2603 |
15 max |
|
| Specific Gravity 60 F / 60 F, ASTM D1429 |
|
0.872 |
| Viscosity Index, ASTM D2270 |
370 |
370 |
| Water Content, mg/kg, ASTM D6304 |
50 (100 max) |
|
| Water, Karl-Fischer, ppm, ASTM D1744 |
|
50 (100 max |